应用范围：项 目Characteristics指 标ValueZSG—1ZSG—2ZSG—3ZSG—4ω（Al2O3）/% &n
PRODUCT DETAILS
|
项 目 Characteristics |
指 标 Value |
|||
| ZSG—1 | ZSG—2 | ZSG—3 | ZSG—4 | |
| ω（Al2O3）/% ≥ | 80 | 75 | 70 | 78 |
| ω（SiC）/% | 6～10 | 6～10 | 0～3 | 2～5 |
| ω（Si3N4）/% | — | — | 6～10 | 4～8 |
| ω（Fe2O3）/% ≤ | 1.0 | 1.0 | 1.0 | 1.0 |
| ω（Si）/% | 3～7 | 3～7 | 3～7 | 3～7 |
| 体积密度/（g/cm3） Bulk density ≥ | 3.00 | 2.90 | 2.90 | 2.90 |
| 显气孔率/% Apparent porosity ≤ | 15 | 16 | 16 | 16 |
| 常温耐压强度/Mpa Cold compressive strength ≥ | 110 | 90 | 100 | 100 |
|
加热永久线变化（1500℃×2h）/% Linear changes on reheating |
﹢0.1～﹣0.2 | ﹢0.1～﹣0.2 | ﹢0.1～﹣0.2 | ﹢0.1～﹣0.2 |
|
荷重软化开始温度（0.2MPa，0.6%）/℃ Refractoriness under load ≥ |
1680 | 1660 | 1680 | 1660 |
|
抗碱性（强度下降率）/% Alkali resistence (Reduction rate) ≤ |
10 | 15 | 10 | 15 |
|
铁水溶蚀指数/% Molten iron erosion resistence rate ≤ |
2 | 3 | 1.5 | 2 |
|
抗渣性（溶蚀率）/% Slag erosion resistence rate ≤ |
10 | 12 | 10 | 10 |
|
导热系数（800℃）/[W（m·K)] Thermal conductivity |
3～5 | 3～5 | 3～5 | 3～5 |
|
平均热膨胀系数×106（20～1000℃）/℃﹣1 average thermal expansion coefficient |
5～8 | 5～8 | 5～8 | 5～8 |
|
注：抗碱性、铁水溶蚀指数、抗渣性、金属硅含量、导热系数和热膨胀系数根据用户需要提供数据。 Note: Properties such as Alkali resistence,Molten iron erosion rate, Slage resistence rate, Silicon content, Thermal conductivity and Thermal expansion coefficient can be tailored to customers' specifications |
||||